Sikafloor®-264
Multi-purpose coloured epoxy resin
Sikafloor®-264 is a 2-component, multi-purpose, coloured epoxy resin.
Sikafloor®- 264 meets the requirements of EN 13813 "Screed materials" and EN 1504- 2 "Concrete surface protection systems".
- Good chemical and mechanical resistance
- Easy application
- Economic
- Liquid proof
- Gloss finish
- Slip resistant surface possible
Utilisation
Film-forming coating for the protection of floors of average traffic, in particular in the following areas:▪ Storage and assembly halls,
▪ Maintenance workshops,
▪ Car parks
Self-smothing and non-slip systems for the protection of industrial floors and floors with very high loads, in particular in the following areas:
▪ Storage and assembly halls
▪ Laboratories, manufacturing
▪ Maintenance workshops
▪ Car parks
▪ Loading ramps Can be used for vertical surfaces by adding Sika Extender T (see PDS)
Avantages
- Good chemical and mechanical resistance
- Easy application
- Economic
- Liquid proof
- Gloss finish
- Slip resistant surface possible
Emballage
| Part A | 15,8 kg containers |
| Part B | 4,2 kg containers |
| Part A+B | 20 kg ready to mix units |
Couleur
| Resin - part A | coloured, liquid |
| Hardener - part B | transparent, liquid |
| Extended colour range |
RAL 1001, 6021, 7030, 7032, 7035, 7037, 7038, 7040, 7042, 9002
Other colours on request.
Détails produits
AGRÉMENTS / NORMES
▪ Test report
▪ CNERIB ref: DTEM / 255/2015
▪ Reaction to fire
European fire classification according to EN standard
13501-1: Bfl-S1
▪ Technical advice
▪ Technical Advice n ° 12 / 18-1774_V1:
UPEC classification U4, P3, E2 / 3, C2 and U4, P4, E2 / 3, C2
▪ Kitchen Technical Advice n ° 12 / 18-1775_V1:
UPEC classification U4, P4S, E2 / 3, C2
▪ CSTB performance ranking
Sika EpoxyFloor ESli4 System
| i | p | r | u | a1 | a2 | b1 | b2 | s1 | s2 | s3 | s4 | s5 |
| 2 | 3 | 2 | 4 | 3 | 3 | 3 | 3 | 3 | 3 | 3 | 3 | 3 |
▪ Slip resistance
* R10 Classification according to DIN 51130 (with addition of Sikagrip)
* PC10 classification according to the XP P 05-011 standard (with addition of Sikagrip)
▪ Indoor air quality
Emissions to indoor air - Classification A + (very low emissions)
▪ Food atmosphere
ISEGA Laboratory Test Report No. 36314 U13
▪ Action of microorganisms
▪ ISO 846 standard: Good result
▪ Clean rooms
▪ISO Class 4 (Particles) classification according to standard
EN ISO 14644-1
▪ISO Classification Class -6.5 (VOC) according to EN standard
ISO 14644-8
▪ Adapted to the G.M.P. AT
|
|
|
Base chimique
Epoxy resin
Durée de Conservation
24 months from date of production
Conditions de Stockage
The product must be stored in original, unopened and undamaged sealed packaging in dry conditions at temperatures between +5 °C and +30 °C.
Densité
| Part A | ~ 1,64 kg/l |
| Part B | ~ 1,00 kg/l |
| Mixed resin | ~ 1,40 kg/l |
All Density values at +23 °C.
Teneur en Matière sèche en Volume
~100 %
Teneur en Matière sèche en Poids
~100 %
Dureté Shore D
| ~76 (7 days / +23 °C) | (DIN 53 505) |
Résistance à l’Abrasion
| ~35 mg (CS 10/1000/1000) (7 days / +23 °C) | (DIN 53109) |
Résistance en Compression
| ~53 N/mm2 (Resin filled 1:0.9 with F34) (28 days / +23 °C) | (EN196-1) |
Résistance à la Flexion
| ~20 N/mm2 (Resin filled 1:0.9 with F34) (28 days / +23 °C) | (EN 196-1) |
Adhérence par Traction directe
| > 1,5 N/mm² (failure in concrete) | (ISO 4624) |
Résistance chimique
Resistant to many chemicals. Contact Sika technical service for specific information.
Résistance thermique
| Exposure | Dry heat |
| Permanent | +50 °C |
| Short-term max. 7 d | +80 °C |
| Short-term max. 12 h | +100 °C |
Short-term moist/wet heat up to +80 °C where exposure is only occasional (steam cleaning etc.).
Application
Proportions du Mélange
Part A : part B = 79 : 21 (by weight)
Température de l'Air Ambiant
+10 °C min. / +30 °C max.
Humidité relative de l’Air
80 % r.h. max.
Point de Rosée
Beware of condensation!
The substrate and uncured floor must be at least 3 °C above dew point to reduce the risk of condensation.
Température du Support
+10 °C min. / +30 °C max.
Humidité du Support
< 4 % pbw moisture content.
Test method: Sika®-Tramex meter, CM-measurement or Oven-dry-method.
No rising moisture according to ASTM (Polyethylene-sheet).
Durée Pratique d'Utilisation
| Temperature | Pot life |
| +10 °C | ~ 50 minutes |
| +20 °C | ~ 25 minutes |
| +30 °C | ~ 15 minutes |
Vitesse de Durcissement
Before applying Sikafloor®-264 on Sikafloor®-264:
| Substrate temperature | Minimum | Maximum |
| +10 °C | 30 hours | 3 days |
| +20 °C | 24 hours | 2 days |
| +30 °C | 16 hours | 1 days |
Hardening time :
| Temperature | Foot traffic | Light traffic | Full cure |
| +10 °C | ~ 72 hours | ~ 6 days | ~ 10 days |
| +20 °C | ~ 24 hours | ~ 4 days | ~ 7 days |
| +30 °C | ~ 18 hours | ~ 2 days | ~ 5 days |
Note: These data are only indicative as the curing times vary according to the drying conditions (Particularly temperature and relative humidity)
Consommation
| Coating | Product | Consumption |
| Primary | 1-2 Sikafloor®- 160/161 | ~ 0.35 – 0.55 kg/m² |
| Grout-Mortar | If necessary | Refer to the technical data sheet of Sikafloor®- 160/161 |
| Filmogenic | 2 x Sikafloor®-264 | ~ 0.25 – 0.30 kg/m² |
| Structure | Refer to the technical data sheet for Sikafloor®-264 N Thixo | |
| Colored quartz (~ 4 mm) | 1 p / p Sikafloor®-263 SL + 1 p / p Sika Silifloor- 250 0.1- 0.3 mm + broadcast abundantly Sika Quartz 0,4- 0,9 mm ou 0,7-1,3 mm + Sikafloor®-264 | ~ 2 kg/m² ~ 2 kg/m² ~ 6 kg/m² ~ 0,7 kg/m² |
| Self-smoothing | 1 p / p Sikafloor®-264 + 1 p / p Sika Silifloor- 250 0.1- 0.3 mm | ~ 1.9 kg / m² / mm of the mixture |
p / p. : share by weight
These are theoretical values which do not take into account a certain
number of elements that can increase them such as porosity, roughness,
losses, etc ..?
MÉLANGE
Prior to mixing, stir part A mechanically. When all of part B has been added to part A, mix continuously for 3 minutes until a uniform mix has been achieved. When parts A and B have been mixed, add the quartz sand and if required the Extender T and mix for a further 2 minutes until a uniform mix has been achieved. To ensure thorough mixing pour materials into another container and mix again to achieve a consistent mix. Over mixing must be avoided to minimise air entrainment.
Mixing Tools
Sikafloor®-264 must be thoroughly mixed using a low speed electric stirrer (300 - 400 rpm) or other suitable equipment. For the preparation of mortars use a forced action mixer of rotating pan, paddle or trough type. Don't use free fall mixers.
APPLICATION
Check substrate moisture, relative humidity, ambient product and substrate temperatures and dew point.
If the substrate moisture content is > 4%, the Sikafloor® -EpoCem® system can be used to form a temporary rising damp barrier.
Substrate defects must be addressed first. Refer to Sikafloor® -144/160/161 Technical Data Sheet.
Film-forming coating
Apply Sikafloor® -264 in two crossed coats by roller.
Anti-slip coating
Apply Sikafloor®-264 with a rubber squeegee and finish with a roller.
Self-smoothing coating
Spread the mixture evenly with a serrated trowel.
Wear nail shoes, and use Spiked roller in cross passes while the resin is still fresh.
NETTOYAGE DES OUTILS
Clean all tools and application equipment with Thinner C immediately after use. Hardened and/or cured material can only be removed mechanically.